{"id":2769,"date":"2026-07-23T08:15:56","date_gmt":"2026-07-23T08:15:56","guid":{"rendered":"https:\/\/zhiweichem.com\/?p=2769"},"modified":"2026-07-23T08:15:56","modified_gmt":"2026-07-23T08:15:56","slug":"hydrophobically-modified-hydroxyethyl-cellulose","status":"publish","type":"post","link":"https:\/\/zhiweichem.com\/pt\/hmhec\/hydrophobically-modified-hydroxyethyl-cellulose\/","title":{"rendered":"De que forma \u00e9 que a hidroxietilcelulose modificada hidrofobicamente engrossa a tinta?"},"content":{"rendered":"<figure class=\"wp-block-image aligncenter size-large\"><img fetchpriority=\"high\" decoding=\"async\" width=\"1024\" height=\"576\" data-src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-for-Water-Based-Paint-1024x576.webp\" src=\"data:image\/gif;base64,R0lGODlhAQABAIAAAAAAAP\/\/\/yH5BAEAAAAALAAAAAABAAEAAAIBRAA7\" alt=\"Hidroxietilcelulose modificada hidrofobicamente para tintas\" class=\"wp-image-2775 lazyload\"\/><noscript><img decoding=\"async\" width=\"1024\" height=\"576\" src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-for-Water-Based-Paint-1024x576.webp\" alt=\"Hidroxietilcelulose modificada hidrofobicamente para tintas\" class=\"wp-image-2775\" srcset=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-for-Water-Based-Paint-1024x576.webp 1024w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-for-Water-Based-Paint-300x169.webp 300w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-for-Water-Based-Paint-768x432.webp 768w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-for-Water-Based-Paint-1536x864.webp 1536w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-for-Water-Based-Paint-18x10.webp 18w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-for-Water-Based-Paint.webp 1891w\" sizes=\"(max-width: 1024px) 100vw, 1024px\" \/><\/noscript><\/figure>\n\n\n\n<p class=\"wp-block-paragraph\">A hidroxietilcelulose modificada hidrofobicamente espessa a tinta \u00e0 base de \u00e1gua atrav\u00e9s de dois mecanismos interligados.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A sua estrutura principal de celulose sol\u00favel em \u00e1gua hidrata-se e aumenta a viscosidade da fase aquosa. Os seus grupos laterais hidrof\u00f3bicos tamb\u00e9m se associam entre si e com superf\u00edcies hidrof\u00f3bicas no revestimento. Estas intera\u00e7\u00f5es criam uma rede tridimensional tempor\u00e1ria.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A rede pode incluir cadeias de pol\u00edmeros, part\u00edculas de l\u00e1tex, carbonato de c\u00e1lcio, caulim, tensioativos e outros componentes da formula\u00e7\u00e3o. Proporciona uma elevada viscosidade em repouso, mas pode separar-se sob cisalhamento e recompor-se ap\u00f3s a diminui\u00e7\u00e3o da for\u00e7a de cisalhamento.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Esta estrutura revers\u00edvel explica por que raz\u00e3o a hidroxietilcelulose modificada hidrofobicamente permite a suspens\u00e3o do pigmento, a estabilidade de armazenamento, a resist\u00eancia ao escorrimento, o toque do pincel e um fluxo de aplica\u00e7\u00e3o controlado.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">No entanto, o desempenho do HMHEC depende fortemente da concentra\u00e7\u00e3o do pol\u00edmero, do tipo de pigmento, do tamanho das part\u00edculas, da temperatura, do n\u00edvel de eletr\u00f3lito, do pacote de dispersantes e do hist\u00f3rico de cisalhamento. Um tipo de HMHEC que apresenta um bom desempenho numa tinta pode comportar-se de forma diferente noutra.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">O que \u00e9 a hidroxietilcelulose modificada hidrofobicamente?<\/h2>\n\n\n\n<p class=\"wp-block-paragraph\">A hidroxietilcelulose modificada hidrofobicamente \u00e9 normalmente abreviada como HMHEC.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">O HMHEC tem como estrutura principal a hidroxietilcelulose. Em seguida, o fabricante introduz uma pequena quantidade de grupos hidrof\u00f3bicos nessa estrutura.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">O pol\u00edmero resultante apresenta uma estrutura anfif\u00edlica:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>A estrutura principal da hidroxietilcelulose interage com a \u00e1gua.<\/li>\n\n\n\n<li>Os grupos hidrof\u00f3bicos evitam o contacto direto com a \u00e1gua.<\/li>\n\n\n\n<li>Os grupos hidrof\u00f3bicos de diferentes cadeias polim\u00e9ricas associam-se entre si.<\/li>\n\n\n\n<li>Alguns grupos hidrof\u00f3bicos podem interagir com part\u00edculas de l\u00e1tex e outros componentes hidrof\u00f3bicos da formula\u00e7\u00e3o.<\/li>\n<\/ul>\n\n\n\n<p class=\"wp-block-paragraph\">Estas liga\u00e7\u00f5es tempor\u00e1rias aumentam o tamanho efetivo da estrutura do pol\u00edmero em solu\u00e7\u00e3o. Al\u00e9m disso, criam liga\u00e7\u00f5es cruzadas f\u00edsicas entre as cadeias polim\u00e9ricas.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">As liga\u00e7\u00f5es n\u00e3o s\u00e3o liga\u00e7\u00f5es qu\u00edmicas permanentes. O cisalhamento pode romp\u00ea-las, e estas podem voltar a formar-se assim que o cisalhamento diminuir.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">HMHEC versus HEC convencional<\/h2>\n\n\n\n<p class=\"wp-block-paragraph\">A hidroxietilcelulose convencional e a HMHEC est\u00e3o relacionadas, mas n\u00e3o espessam exatamente atrav\u00e9s do mesmo mecanismo.<\/p>\n\n\n\n<figure class=\"wp-block-table\"><table class=\"has-fixed-layout\"><thead><tr><th>Im\u00f3veis<\/th><th>HEC convencional<\/th><th>HMHEC<\/th><\/tr><\/thead><tbody><tr><td>Estrutura do pol\u00edmero<\/td><td>\u00c9ter de celulose hidrof\u00edlico<\/td><td>\u00c9ter de celulose hidrof\u00edlico com grupos hidrof\u00f3bicos<\/td><\/tr><tr><td>Principal mecanismo de espessamento<\/td><td>Hidrata\u00e7\u00e3o, expans\u00e3o da cadeia e emaranhamento<\/td><td>Hidrata\u00e7\u00e3o, entrela\u00e7amento e associa\u00e7\u00e3o hidrof\u00f3bica<\/td><\/tr><tr><td>Intera\u00e7\u00e3o com o l\u00e1tex<\/td><td>Efeito associativo limitado<\/td><td>Pode associar-se a superf\u00edcies de l\u00e1tex hidrof\u00f3bicas<\/td><\/tr><tr><td>Intera\u00e7\u00e3o com pigmentos<\/td><td>Adsor\u00e7\u00e3o e liga\u00e7\u00f5es de hidrog\u00e9nio<\/td><td>Adsor\u00e7\u00e3o, liga\u00e7\u00f5es de hidrog\u00e9nio e associa\u00e7\u00e3o hidrof\u00f3bica<\/td><\/tr><tr><td>Viscosidade a baixo cisalhamento<\/td><td>Depende principalmente do peso molecular e da concentra\u00e7\u00e3o<\/td><td>Pode receber apoio adicional de uma rede associativa<\/td><\/tr><tr><td>Resposta ao cisalhamento<\/td><td>Viscosidade decrescente sob cisalhamento<\/td><td>Frequentemente, observa-se uma maior dilui\u00e7\u00e3o por cisalhamento a baixos n\u00edveis de cisalhamento<\/td><\/tr><tr><td>Recupera\u00e7\u00e3o<\/td><td>As cadeias de pol\u00edmeros reorganizam-se gradualmente<\/td><td>As jun\u00e7\u00f5es hidrof\u00f3bicas podem reformar-se ap\u00f3s a cisalhamento<\/td><\/tr><tr><td>Sensibilidade da f\u00f3rmula<\/td><td>Influenciado pela \u00e1gua, pelo pH, pelos sais e pelos s\u00f3lidos<\/td><td>Tamb\u00e9m sens\u00edvel a tensioativos, ao tipo de l\u00e1tex e a componentes hidrof\u00f3bicos<\/td><\/tr><\/tbody><\/table><\/figure>\n\n\n\n<p class=\"wp-block-paragraph\">Um HEC convencional de alta viscosidade pode apresentar maior viscosidade do que um HMHEC de baixa viscosidade numa solu\u00e7\u00e3o simples de \u00e1gua. Este resultado n\u00e3o significa que o HEC convencional apresente o mesmo comportamento associativo num revestimento acabado.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A curva reol\u00f3gica completa \u00e9 mais importante do que um \u00fanico valor de viscosidade.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Como se forma a rede associativa da HMHEC?<\/h2>\n\n\n\n<figure class=\"wp-block-image aligncenter size-large\"><img decoding=\"async\" width=\"1024\" height=\"576\" data-src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Associative-Network-1024x576.webp\" src=\"data:image\/gif;base64,R0lGODlhAQABAIAAAAAAAP\/\/\/yH5BAEAAAAALAAAAAABAAEAAAIBRAA7\" alt=\"Mecanismo de espessamento associativo do HMHEC\" class=\"wp-image-2773 lazyload\"\/><noscript><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Associative-Network-1024x576.webp\" alt=\"Mecanismo de espessamento associativo do HMHEC\" class=\"wp-image-2773\" srcset=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Associative-Network-1024x576.webp 1024w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Associative-Network-300x169.webp 300w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Associative-Network-768x432.webp 768w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Associative-Network-1536x864.webp 1536w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Associative-Network-18x10.webp 18w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Associative-Network.webp 1891w\" sizes=\"(max-width: 1024px) 100vw, 1024px\" \/><\/noscript><\/figure>\n\n\n\n<p class=\"wp-block-paragraph\">O processo de espessamento pode ser dividido em cinco fases.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">1. A estrutura de celulose hidrata-se<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">A \u00e1gua envolve os grupos hidroxietilo e faz com que as cadeias polim\u00e9ricas se expandam.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">As cadeias expandidas ocupam um maior volume hidrodin\u00e2mico. Este fen\u00f3meno aumenta a viscosidade da fase aquosa, mesmo antes de se desenvolver uma forte associa\u00e7\u00e3o hidrof\u00f3bica.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">2. Os grupos hidrof\u00f3bicos movem-se em conjunto<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Os grupos hidrof\u00f3bicos t\u00eam baixa afinidade pela \u00e1gua. Tendem a agrupar-se em pequenos dom\u00ednios hidrof\u00f3bicos.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">V\u00e1rios grupos provenientes de diferentes cadeias polim\u00e9ricas podem unir-se ao mesmo dom\u00ednio. Cada dom\u00ednio funciona como um ponto de jun\u00e7\u00e3o tempor\u00e1rio.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">3. A associa\u00e7\u00e3o intermolecular cria uma rede<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Quando a concentra\u00e7\u00e3o do pol\u00edmero atinge um n\u00edvel suficientemente elevado, os grupos hidrof\u00f3bicos presentes em cadeias separadas formam uma rede interligada.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A rede pode reter \u00e1gua e retardar o movimento das part\u00edculas de pigmento e de carga. Tamb\u00e9m pode aumentar a viscosidade a baixo cisalhamento.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A formula\u00e7\u00e3o pode apresentar uma resposta de espessamento mais acentuada depois de a concentra\u00e7\u00e3o do pol\u00edmero ultrapassar um intervalo cr\u00edtico de associa\u00e7\u00e3o.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">4. O HMHEC \u00e9 adsorvido nas part\u00edculas da formula\u00e7\u00e3o<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Grupos hidroxilo no <a href=\"https:\/\/en.wikipedia.org\/wiki\/Ethyl_methyl_cellulose\" target=\"_blank\" data-type=\"link\" data-id=\"https:\/\/en.wikipedia.org\/wiki\/Ethyl_methyl_cellulose\" rel=\"noreferrer noopener\">celulose<\/a> A estrutura principal pode interagir com superf\u00edcies minerais atrav\u00e9s de liga\u00e7\u00f5es de hidrog\u00e9nio e outras for\u00e7as f\u00edsicas.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Os grupos hidrof\u00f3bicos tamb\u00e9m podem interagir com regi\u00f5es adequadas da superf\u00edcie ou com materiais org\u00e2nicos adsorvidos.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Uma cadeia de HMHEC pode entrar em contacto com mais do que uma part\u00edcula. Esta estrutura cria pontes polim\u00e9ricas entre as part\u00edculas.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">5. A estrutura reage ao cisalhamento<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Um baixo cisalhamento permite que mais liga\u00e7\u00f5es hidrof\u00f3bicas se mantenham no seu lugar. O revestimento mant\u00e9m, assim, a estrutura de armazenamento e a suspens\u00e3o.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Um cisalhamento mais elevado rompe algumas liga\u00e7\u00f5es tempor\u00e1rias e alinha as cadeias de pol\u00edmeros na dire\u00e7\u00e3o do fluxo. A viscosidade diminui e o revestimento torna-se mais f\u00e1cil de bombear, aplicar com pincel, rolo ou pulverizar.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Quando o cisalhamento diminui, voltam a formar-se algumas jun\u00e7\u00f5es hidrof\u00f3bicas. A viscosidade recupera-se ent\u00e3o, embora essa recupera\u00e7\u00e3o possa n\u00e3o ser imediata nem completa.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Que for\u00e7as mant\u00eam o HMHEC e os pigmentos unidos?<\/h2>\n\n\n\n<figure class=\"wp-block-image aligncenter size-large\"><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" data-src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Bridging-Pigment-Particles-1024x576.webp\" src=\"data:image\/gif;base64,R0lGODlhAQABAIAAAAAAAP\/\/\/yH5BAEAAAAALAAAAAABAAEAAAIBRAA7\" alt=\"Adsor\u00e7\u00e3o de HMHEC e forma\u00e7\u00e3o de pontes entre as part\u00edculas de pigmento\" class=\"wp-image-2774 lazyload\"\/><noscript><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Bridging-Pigment-Particles-1024x576.webp\" alt=\"Adsor\u00e7\u00e3o de HMHEC e forma\u00e7\u00e3o de pontes entre as part\u00edculas de pigmento\" class=\"wp-image-2774\" srcset=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Bridging-Pigment-Particles-1024x576.webp 1024w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Bridging-Pigment-Particles-300x169.webp 300w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Bridging-Pigment-Particles-768x432.webp 768w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Bridging-Pigment-Particles-1536x864.webp 1536w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Bridging-Pigment-Particles-18x10.webp 18w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Bridging-Pigment-Particles.webp 1891w\" sizes=\"(max-width: 1024px) 100vw, 1024px\" \/><\/noscript><\/figure>\n\n\n\n<p class=\"wp-block-paragraph\">N\u00e3o existe uma \u00fanica for\u00e7a que explique a adsor\u00e7\u00e3o do HMHEC nas part\u00edculas de pigmento.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Podem ocorrer v\u00e1rias intera\u00e7\u00f5es ao mesmo tempo:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>Liga\u00e7\u00f5es de hidrog\u00e9nio<\/li>\n\n\n\n<li>Atra\u00e7\u00e3o de Van der Waals<\/li>\n\n\n\n<li>Atra\u00e7\u00e3o ou repuls\u00e3o eletrost\u00e1tica<\/li>\n\n\n\n<li>Associa\u00e7\u00e3o hidrof\u00f3bica<\/li>\n\n\n\n<li>Emaranhamento de pol\u00edmeros<\/li>\n\n\n\n<li>Liga\u00e7\u00e3o f\u00edsica<\/li>\n\n\n\n<li>Intera\u00e7\u00e3o com dispersantes ou tensioativos adsorvidos<\/li>\n<\/ul>\n\n\n\n<p class=\"wp-block-paragraph\">A import\u00e2ncia relativa de cada for\u00e7a depende da composi\u00e7\u00e3o qu\u00edmica do pigmento, do pH, da for\u00e7a i\u00f4nica, do tamanho das part\u00edculas, do tratamento da superf\u00edcie e da estrutura do pol\u00edmero.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Esta complexidade explica por que raz\u00e3o o carbonato de c\u00e1lcio e o caulim n\u00e3o reagem da mesma forma.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Efeito da concentra\u00e7\u00e3o de HMHEC<\/h2>\n\n\n\n<figure class=\"wp-block-image size-large\"><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" data-src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Critical-Association-Concentration-1024x576.webp\" src=\"data:image\/gif;base64,R0lGODlhAQABAIAAAAAAAP\/\/\/yH5BAEAAAAALAAAAAABAAEAAAIBRAA7\" alt=\"Efeito da concentra\u00e7\u00e3o de HMHEC na adsor\u00e7\u00e3o de pigmentos\" class=\"wp-image-2772 lazyload\"\/><noscript><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Critical-Association-Concentration-1024x576.webp\" alt=\"Efeito da concentra\u00e7\u00e3o de HMHEC na adsor\u00e7\u00e3o de pigmentos\" class=\"wp-image-2772\" srcset=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Critical-Association-Concentration-1024x576.webp 1024w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Critical-Association-Concentration-300x169.webp 300w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Critical-Association-Concentration-768x432.webp 768w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Critical-Association-Concentration-1536x864.webp 1536w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Critical-Association-Concentration-18x10.webp 18w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Critical-Association-Concentration.webp 1891w\" sizes=\"(max-width: 1024px) 100vw, 1024px\" \/><\/noscript><\/figure>\n\n\n\n<p class=\"wp-block-paragraph\">Uma suspens\u00e3o de pigmento em laborat\u00f3rio revelou que a adsor\u00e7\u00e3o de HMHEC aumentava \u00e0 medida que a concentra\u00e7\u00e3o de HMHEC aumentava.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A adsor\u00e7\u00e3o aumentou inicialmente de forma lenta. Posteriormente, registou um aumento acentuado quando a concentra\u00e7\u00e3o de HMHEC atingiu aproximadamente 0,35-0,40 g por 100 mL, o que equivale a 3,5-4,0 mg\/mL.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Esta transi\u00e7\u00e3o sugere que o sistema tinha atingido uma regi\u00e3o de associa\u00e7\u00e3o cr\u00edtica.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Abaixo desta concentra\u00e7\u00e3o, as cadeias polim\u00e9ricas isoladas e os pequenos grupos associativos dominavam a solu\u00e7\u00e3o. Acima dela, a associa\u00e7\u00e3o intermolecular tornou-se muito mais forte.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Os grupos hidrof\u00f3bicos nas cadeias livres de HMHEC podiam ligar-se a grupos presentes nas cadeias que j\u00e1 se tinham adsorvido \u00e0 superf\u00edcie do pigmento. Este comportamento favorecia a adsor\u00e7\u00e3o em m\u00faltiplas camadas e a forma\u00e7\u00e3o de estruturas pol\u00edmero-pigmento de maiores dimens\u00f5es.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A concentra\u00e7\u00e3o exata de transi\u00e7\u00e3o n\u00e3o \u00e9 uma especifica\u00e7\u00e3o universal da HMHEC. Depende dos seguintes fatores:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>Tipo de grupo hidrof\u00f3bico<\/li>\n\n\n\n<li>N\u00edvel de substitui\u00e7\u00e3o hidrof\u00f3bica<\/li>\n\n\n\n<li>Peso molecular do HEC<\/li>\n\n\n\n<li>Concentra\u00e7\u00e3o de pol\u00edmero<\/li>\n\n\n\n<li>\u00c1rea superficial do pigmento<\/li>\n\n\n\n<li>Concentra\u00e7\u00e3o de eletr\u00f3litos<\/li>\n\n\n\n<li>Temperatura<\/li>\n\n\n\n<li>M\u00e9todo de ensaio<\/li>\n<\/ul>\n\n\n\n<p class=\"wp-block-paragraph\">Um revestimento comercial pode atingir uma transi\u00e7\u00e3o associativa numa dosagem diferente.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Efeito da temperatura<\/h2>\n\n\n\n<figure class=\"wp-block-image aligncenter size-large\"><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" data-src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Temperature-Effect-on-HMHEC-Adsorption-1024x576.webp\" src=\"data:image\/gif;base64,R0lGODlhAQABAIAAAAAAAP\/\/\/yH5BAEAAAAALAAAAAABAAEAAAIBRAA7\" alt=\"Efeito da temperatura na adsor\u00e7\u00e3o do pigmento HMHEC\" class=\"wp-image-2771 lazyload\"\/><noscript><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Temperature-Effect-on-HMHEC-Adsorption-1024x576.webp\" alt=\"Efeito da temperatura na adsor\u00e7\u00e3o do pigmento HMHEC\" class=\"wp-image-2771\" srcset=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Temperature-Effect-on-HMHEC-Adsorption-1024x576.webp 1024w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Temperature-Effect-on-HMHEC-Adsorption-300x169.webp 300w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Temperature-Effect-on-HMHEC-Adsorption-768x432.webp 768w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Temperature-Effect-on-HMHEC-Adsorption-1536x864.webp 1536w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Temperature-Effect-on-HMHEC-Adsorption-18x10.webp 18w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Temperature-Effect-on-HMHEC-Adsorption.webp 1891w\" sizes=\"(max-width: 1024px) 100vw, 1024px\" \/><\/noscript><\/figure>\n\n\n\n<p class=\"wp-block-paragraph\">A adsor\u00e7\u00e3o de HMHEC no carbonato de c\u00e1lcio e no caulim diminuiu \u00e0 medida que a temperatura aumentava na suspens\u00e3o modelo.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">V\u00e1rios processos ocorreram ao mesmo tempo.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Uma temperatura mais elevada aumentou o movimento molecular e pode ter exposto uma maior \u00e1rea superficial das part\u00edculas. Estes efeitos poder\u00e3o favorecer a adsor\u00e7\u00e3o.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">No entanto, o aumento da temperatura tamb\u00e9m perturbou as liga\u00e7\u00f5es de hidrog\u00e9nio e os microdom\u00ednios hidrof\u00f3bicos. As mol\u00e9culas de \u00e1gua entraram em competi\u00e7\u00e3o mais intensa com a camada de pol\u00edmero adsorvida. A estrutura associativa tempor\u00e1ria tornou-se mais f\u00e1cil de romper.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Os efeitos negativos predominaram no sistema testado.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A diminui\u00e7\u00e3o da adsor\u00e7\u00e3o tornou-se mais acentuada quando a temperatura ultrapassou os 50 \u00b0C, aproximadamente.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Os formuladores de revestimentos devem, por isso, avaliar o HMHEC tanto \u00e0 temperatura de produ\u00e7\u00e3o como \u00e0 temperatura de armazenamento. Um espessante que confere uma consist\u00eancia firme a 25 \u00b0C pode apresentar um perfil reol\u00f3gico diferente ap\u00f3s uma etapa de fabrico a quente ou um per\u00edodo de armazenamento em ambiente quente.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Efeito da concentra\u00e7\u00e3o de pigmento<\/h2>\n\n\n\n<p class=\"wp-block-paragraph\">A quantidade de HMHEC adsorvida por unidade de pigmento diminuiu \u00e0 medida que a concentra\u00e7\u00e3o do pigmento aumentava.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Uma concentra\u00e7\u00e3o mais elevada de pigmento pode aumentar o contacto e a agrega\u00e7\u00e3o das part\u00edculas. A \u00e1rea superficial espec\u00edfica efetiva pode, ent\u00e3o, diminuir.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">O HMHEC dispon\u00edvel tamb\u00e9m tem de ser distribu\u00eddo por mais part\u00edculas. Cada unidade de pigmento recebe, portanto, menos pol\u00edmero.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Este resultado tem um importante significado pr\u00e1tico. A mesma dosagem de HMHEC pode apresentar um comportamento diferente numa tinta com baixo teor de PVC e numa com elevado teor de PVC.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Um formulador n\u00e3o deve transferir uma dosagem de HMHEC diretamente entre:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>Prim\u00e1rio e acabamento<\/li>\n\n\n\n<li>Tinta mate e tinta semibrilhante<\/li>\n\n\n\n<li>Tinta rica em carbonato de c\u00e1lcio e rica em caulim<\/li>\n\n\n\n<li>Revestimentos com baixo teor de s\u00f3lidos e com elevado teor de s\u00f3lidos<\/li>\n\n\n\n<li>Diferentes distribui\u00e7\u00f5es granulom\u00e9tricas das part\u00edculas de enchimento<\/li>\n<\/ul>\n\n\n\n<p class=\"wp-block-paragraph\">A concentra\u00e7\u00e3o volum\u00e9trica de pigmento e o pacote de diluentes devem ser tidos em conta no processo de sele\u00e7\u00e3o do espessante.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Efeito no tamanho das part\u00edculas de pigmento<\/h2>\n\n\n\n<figure class=\"wp-block-image aligncenter size-large\"><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" data-src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Pigment-Particle-Size-Before-and-After-HMHEC-1024x576.webp\" src=\"data:image\/gif;base64,R0lGODlhAQABAIAAAAAAAP\/\/\/yH5BAEAAAAALAAAAAABAAEAAAIBRAA7\" alt=\"Altera\u00e7\u00e3o do tamanho das part\u00edculas de pigmento ap\u00f3s a adsor\u00e7\u00e3o em HMHEC\" class=\"wp-image-2770 lazyload\"\/><noscript><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Pigment-Particle-Size-Before-and-After-HMHEC-1024x576.webp\" alt=\"Altera\u00e7\u00e3o do tamanho das part\u00edculas de pigmento ap\u00f3s a adsor\u00e7\u00e3o em HMHEC\" class=\"wp-image-2770\" srcset=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Pigment-Particle-Size-Before-and-After-HMHEC-1024x576.webp 1024w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Pigment-Particle-Size-Before-and-After-HMHEC-300x169.webp 300w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Pigment-Particle-Size-Before-and-After-HMHEC-768x432.webp 768w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Pigment-Particle-Size-Before-and-After-HMHEC-1536x864.webp 1536w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Pigment-Particle-Size-Before-and-After-HMHEC-18x10.webp 18w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/Pigment-Particle-Size-Before-and-After-HMHEC.webp 1891w\" sizes=\"(max-width: 1024px) 100vw, 1024px\" \/><\/noscript><\/figure>\n\n\n\n<p class=\"wp-block-paragraph\">A adsor\u00e7\u00e3o por HMHEC alterou o tamanho das part\u00edculas medido tanto nas suspens\u00f5es de carbonato de c\u00e1lcio como nas de caulim.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Numa rela\u00e7\u00e3o de massa HMHEC\/pigmento de 1:10, o raio m\u00e9dio das part\u00edculas relatado variou da seguinte forma:<\/p>\n\n\n\n<figure class=\"wp-block-table\"><table class=\"has-fixed-layout\"><thead><tr><th>Pigmento<\/th><th>Antes da adsor\u00e7\u00e3o por HMHEC<\/th><th>Ap\u00f3s a adsor\u00e7\u00e3o por HMHEC<\/th><th>Interpreta\u00e7\u00e3o principal<\/th><\/tr><\/thead><tbody><tr><td>Carbonato de c\u00e1lcio<\/td><td>83,12 nm<\/td><td>196,40 nm<\/td><td>Forte adsor\u00e7\u00e3o e forma\u00e7\u00e3o de pontes entre pol\u00edmeros<\/td><\/tr><tr><td>Caulim<\/td><td>244,40 nm<\/td><td>319,50 nm<\/td><td>Verificou-se adsor\u00e7\u00e3o, mas o aumento foi menor<\/td><\/tr><\/tbody><\/table><\/figure>\n\n\n\n<p class=\"wp-block-paragraph\">O aumento do tamanho das part\u00edculas n\u00e3o significa que o HMHEC tenha simplesmente provocado uma flocula\u00e7\u00e3o descontrolada do pigmento.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Um instrumento de medi\u00e7\u00e3o do tamanho das part\u00edculas por laser deteta a estrutura hidrodin\u00e2mica que se desloca atrav\u00e9s do l\u00edquido. As camadas de pol\u00edmero adsorvidas, as pontes de pol\u00edmero e os aglomerados revers\u00edveis de pigmento e pol\u00edmero podem, todos eles, aumentar o tamanho aparente.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Uma rede controlada pode contribuir para a estabilidade da suspens\u00e3o. A forma\u00e7\u00e3o excessiva de pontes pode provocar flocula\u00e7\u00e3o prejudicial, um desenvolvimento deficiente da cor, menor brilho ou maior tens\u00e3o de escoamento.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">O formulador deve distinguir entre uma associa\u00e7\u00e3o estrutural \u00fatil e a agrega\u00e7\u00e3o descontrolada de pigmentos.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Por que raz\u00e3o o HMHEC interage mais fortemente com o carbonato de c\u00e1lcio?<\/h2>\n\n\n\n<p class=\"wp-block-paragraph\">O sistema laboratorial revelou uma adsor\u00e7\u00e3o mais forte do HMHEC no carbonato de c\u00e1lcio do que no caulim.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">V\u00e1rios fatores contribu\u00edram para essa diferen\u00e7a.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Tamanho das part\u00edculas mais pequeno<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O carbonato de c\u00e1lcio testado apresentava um tamanho de part\u00edcula inicial mais pequeno. Por conseguinte, proporcionava uma maior \u00e1rea superficial para a adsor\u00e7\u00e3o do pol\u00edmero.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Qu\u00edmica de Superf\u00edcies<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O carbonato de c\u00e1lcio e o caulim apresentam grupos superficiais e comportamentos de carga diferentes. Estas diferen\u00e7as afetam as liga\u00e7\u00f5es de hidrog\u00e9nio e as intera\u00e7\u00f5es eletrost\u00e1ticas.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">I\u00f5es de c\u00e1lcio<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Os i\u00f5es de c\u00e1lcio podem alterar o ambiente el\u00e9trico junto \u00e0 superf\u00edcie da part\u00edcula. Podem comprimir a dupla camada el\u00e9trica e reduzir parte da repuls\u00e3o eletrost\u00e1tica.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A associa\u00e7\u00e3o hidrof\u00f3bica pode, assim, ter um impacto maior na intera\u00e7\u00e3o total.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Estrutura do caulim<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O caulim apresenta normalmente uma estrutura em forma de placa. As suas faces e arestas podem apresentar comportamentos de carga diferentes.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Por volta do pH 9, a repuls\u00e3o eletrost\u00e1tica entre partes da superf\u00edcie do caulim e o pol\u00edmero pode limitar a adsor\u00e7\u00e3o. O resultado exato depende da origem do caulim, do tamanho das part\u00edculas, do tratamento da superf\u00edcie e do pH.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A conclus\u00e3o n\u00e3o deve ser simplificada para \u201cO HMHEC funciona sempre melhor com carbonato de c\u00e1lcio\u201d. Cada lote de pigmento comercial requer testes.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">O que indica o potencial zeta?<\/h2>\n\n\n\n<p class=\"wp-block-paragraph\">O potencial zeta ajuda a descrever o estado el\u00e9trico na proximidade das superf\u00edcies das part\u00edculas dispersas.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Os sistemas de carbonato de c\u00e1lcio e caulim apresentaram tend\u00eancias diferentes ap\u00f3s a adi\u00e7\u00e3o de HMHEC:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>O potencial zeta absoluto do carbonato de c\u00e1lcio aumentou, de um modo geral.<\/li>\n\n\n\n<li>O potencial zeta absoluto do caulim diminuiu, de um modo geral.<\/li>\n<\/ul>\n\n\n\n<p class=\"wp-block-paragraph\">As diferentes tend\u00eancias levam \u00e0 conclus\u00e3o de que o HMHEC interage com os dois pigmentos atrav\u00e9s de diferentes combina\u00e7\u00f5es de for\u00e7as.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Um resultado do potencial zeta, por si s\u00f3, n\u00e3o pode comprovar se a estabilidade do revestimento \u00e9 boa ou fraca. Os pol\u00edmeros associativos podem proporcionar estabiliza\u00e7\u00e3o est\u00e9rica, forma\u00e7\u00e3o de pontes, forma\u00e7\u00e3o de redes e tens\u00e3o de escoamento, aspetos que uma simples medi\u00e7\u00e3o el\u00e9trica n\u00e3o descreve na \u00edntegra.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">O formulador deve combinar o potencial zeta com:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>An\u00e1lise granulom\u00e9trica<\/li>\n\n\n\n<li>Ensaios de sedimenta\u00e7\u00e3o<\/li>\n\n\n\n<li>Reologia<\/li>\n\n\n\n<li>Quedas<\/li>\n\n\n\n<li>Brilho<\/li>\n\n\n\n<li>Intensidade da cor<\/li>\n\n\n\n<li>Estabilidade de armazenamento<\/li>\n\n\n\n<li>Microscopia<\/li>\n<\/ul>\n\n\n\n<h2 class=\"wp-block-heading\">Como \u00e9 que o HMHEC reage ao cisalhamento?<\/h2>\n\n\n\n<p class=\"wp-block-paragraph\">Tanto o HEC como o HMHEC apresentam um comportamento de dilui\u00e7\u00e3o por cisalhamento.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A baixos n\u00edveis de cisalhamento, o HEC convencional forma uma estrutura polim\u00e9rica entrela\u00e7ada. O aumento do cisalhamento rompe parte dessa estrutura e alinha as cadeias polim\u00e9ricas na dire\u00e7\u00e3o do fluxo.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">O HMHEC cont\u00e9m uma rede associativa adicional. Um baixo cisalhamento permite que as liga\u00e7\u00f5es hidrof\u00f3bicas conectem v\u00e1rias cadeias.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Quando o cisalhamento aumenta, estas liga\u00e7\u00f5es f\u00edsicas fr\u00e1geis separam-se. A viscosidade do HMHEC pode, por conseguinte, diminuir mais rapidamente durante o aumento inicial da taxa de cisalhamento.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A um cisalhamento mais elevado, a curva de viscosidade torna-se mais plana, uma vez que grande parte da rede tempor\u00e1ria j\u00e1 foi rompida.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Este comportamento pode proporcionar:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>Elevada viscosidade durante o armazenamento<\/li>\n\n\n\n<li>Bombeamento mais f\u00e1cil durante a produ\u00e7\u00e3o<\/li>\n\n\n\n<li>Fluxo controlado do pincel e do rolo<\/li>\n\n\n\n<li>Menor resist\u00eancia durante a aplica\u00e7\u00e3o em condi\u00e7\u00f5es de alto cisalhamento<\/li>\n\n\n\n<li>Recupera\u00e7\u00e3o da viscosidade ap\u00f3s a aplica\u00e7\u00e3o<\/li>\n<\/ul>\n\n\n\n<p class=\"wp-block-paragraph\">A solu\u00e7\u00e3o de HMHEC testada apresentava uma concentra\u00e7\u00e3o de aproximadamente 0,4 g por 100 mL, ou 0,4% p\/v.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Quando a taxa de cisalhamento diminuiu, a viscosidade voltou a aumentar. A curva de retorno n\u00e3o seguiu exatamente a curva original. A diferen\u00e7a demonstrou que a reconstru\u00e7\u00e3o da rede exigia tempo.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Esta histerese \u00e9 importante nos revestimentos. Um sistema que recupere demasiado depressa pode apresentar um nivelamento deficiente. Um sistema que recupere demasiado lentamente pode apresentar afundamento.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Como o HMHEC afeta o desempenho do revestimento<\/h2>\n\n\n\n<figure class=\"wp-block-table\"><table class=\"has-fixed-layout\"><thead><tr><th>Fase de revestimento<\/th><th>Reologia exigida<\/th><th>Poss\u00edvel contribui\u00e7\u00e3o da HMHEC<\/th><\/tr><\/thead><tbody><tr><td>Armazenamento<\/td><td>Viscosidade elevada a baixo cisalhamento<\/td><td>Suspens\u00e3o de pigmentos e controlo da sin\u00e9rese<\/td><\/tr><tr><td>Mistura<\/td><td>Viscosidade reduzida sob cisalhamento<\/td><td>Maior facilidade de dispers\u00e3o e bombagem<\/td><\/tr><tr><td>Recheio<\/td><td>Fluxo est\u00e1vel e repet\u00edvel<\/td><td>Enchimento de embalagens mais consistente<\/td><\/tr><tr><td>Escovagem<\/td><td>Viscosidade controlada a cisalhamento m\u00e9dio<\/td><td>Melhor arrasto do pincel e forma\u00e7\u00e3o da camada de tinta<\/td><\/tr><tr><td>Rolando<\/td><td>Equil\u00edbrio entre o fluxo e o corpo<\/td><td>Melhor sensa\u00e7\u00e3o ao rolar e melhor controlo das salpicos<\/td><\/tr><tr><td>Pulveriza\u00e7\u00e3o<\/td><td>Menor viscosidade em condi\u00e7\u00f5es de elevado cisalhamento<\/td><td>Melhor atomiza\u00e7\u00e3o quando est\u00e1 corretamente equilibrada<\/td><\/tr><tr><td>Ap\u00f3s a aplica\u00e7\u00e3o<\/td><td>Recupera\u00e7\u00e3o controlada<\/td><td>Resist\u00eancia \u00e0 deforma\u00e7\u00e3o sem perda excessiva de nivelamento<\/td><\/tr><\/tbody><\/table><\/figure>\n\n\n\n<p class=\"wp-block-paragraph\">Normalmente, nenhum espessante, por si s\u00f3, \u00e9 ideal para todas as faixas de cisalhamento.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Um revestimento pode utilizar HMHEC em conjunto com HEC convencional, HEUR, pol\u00edmeros expans\u00edveis em ambiente alcalino, argilas ou outros modificadores reol\u00f3gicos. Esta combina\u00e7\u00e3o permite ajustar com maior precis\u00e3o a viscosidade em condi\u00e7\u00f5es de baixo, m\u00e9dio e alto cisalhamento.<\/p>\n\n\n\n<figure class=\"wp-block-image size-large\"><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" data-src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Shear-Thinning-and-Recovery-1024x576.webp\" src=\"data:image\/gif;base64,R0lGODlhAQABAIAAAAAAAP\/\/\/yH5BAEAAAAALAAAAAABAAEAAAIBRAA7\" alt=\"Redu\u00e7\u00e3o da viscosidade por cisalhamento e recupera\u00e7\u00e3o da viscosidade do HMHEC\" class=\"wp-image-2776 lazyload\"\/><noscript><img loading=\"lazy\" decoding=\"async\" width=\"1024\" height=\"576\" src=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Shear-Thinning-and-Recovery-1024x576.webp\" alt=\"Redu\u00e7\u00e3o da viscosidade por cisalhamento e recupera\u00e7\u00e3o da viscosidade do HMHEC\" class=\"wp-image-2776\" srcset=\"https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Shear-Thinning-and-Recovery-1024x576.webp 1024w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Shear-Thinning-and-Recovery-300x169.webp 300w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Shear-Thinning-and-Recovery-768x432.webp 768w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Shear-Thinning-and-Recovery-1536x864.webp 1536w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Shear-Thinning-and-Recovery-18x10.webp 18w, https:\/\/zhiweichem.com\/wp-content\/uploads\/2026\/07\/HMHEC-Shear-Thinning-and-Recovery.webp 1891w\" sizes=\"(max-width: 1024px) 100vw, 1024px\" \/><\/noscript><figcaption class=\"wp-element-caption\">Uma curva de viscosidade que mostra uma elevada viscosidade a baixo cisalhamento, uma redu\u00e7\u00e3o da viscosidade \u00e0 medida que o cisalhamento aumenta e uma recupera\u00e7\u00e3o parcial quando a taxa de cisalhamento diminui.<\/figcaption><\/figure>\n\n\n\n<h2 class=\"wp-block-heading\">Vari\u00e1veis que influenciam o desempenho do HMHEC<\/h2>\n\n\n\n<h3 class=\"wp-block-heading\">N\u00edvel de modifica\u00e7\u00e3o hidrof\u00f3bica<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Um baixo n\u00edvel de modifica\u00e7\u00e3o pode resultar numa associa\u00e7\u00e3o fraca. Um n\u00edvel elevado pode reduzir a solubilidade na \u00e1gua ou provocar uma intera\u00e7\u00e3o excessiva com o l\u00e1tex e os tensioativos.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Peso molecular do pol\u00edmero<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Um peso molecular mais elevado aumenta normalmente o volume hidrodin\u00e2mico e o entrela\u00e7amento. No entanto, tamb\u00e9m pode aumentar a viscosidade e reduzir o nivelamento.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Tipo de encaderna\u00e7\u00e3o<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">As diferentes part\u00edculas de acr\u00edlico, estireno-acr\u00edlico, acetato de vinilo e outros l\u00e1tex proporcionam superf\u00edcies hidrof\u00f3bicas distintas.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Pacote de pigmentos e extensores<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O carbonato de c\u00e1lcio, o caulim, o di\u00f3xido de tit\u00e2nio, o talco e a s\u00edlica apresentam diferentes propriedades qu\u00edmicas superficiais e tamanhos de part\u00edculas.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Tensioativos e dispersantes<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Os tensioativos podem ocupar s\u00edtios hidrof\u00f3bicos e alterar a rede de associa\u00e7\u00e3o. Os dispersantes podem competir com o HMHEC pelas superf\u00edcies dos pigmentos.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Eletr\u00f3litos<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Os sais alteram a dupla camada el\u00e9trica e a conforma\u00e7\u00e3o do pol\u00edmero. Os i\u00f5es divalentes podem provocar uma resposta diferente da dos sais de s\u00f3dio.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Temperatura<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Temperaturas mais elevadas podem enfraquecer a adsor\u00e7\u00e3o e alterar a viscosidade da solu\u00e7\u00e3o.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Hist\u00f3rico de cisalhamento<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">A dispers\u00e3o a alta velocidade pode interromper temporariamente a rede. A viscosidade medida depende do tempo de recupera\u00e7\u00e3o antes do ensaio.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Ordem de adi\u00e7\u00e3o<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O HMHEC pode apresentar um comportamento diferente quando adicionado antes da dispers\u00e3o do pigmento, ap\u00f3s a dilui\u00e7\u00e3o ou na forma de solu\u00e7\u00e3o pr\u00e9-hidratada.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Plano de Avalia\u00e7\u00e3o do Laborat\u00f3rio HMHEC<\/h2>\n\n\n\n<p class=\"wp-block-paragraph\">Um laborat\u00f3rio de revestimentos deve comparar o HMHEC com o HEC convencional nas mesmas condi\u00e7\u00f5es.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Passo 1: Preparar uma amostra de controlo sem espessante<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">A amostra de controlo mostra a sedimenta\u00e7\u00e3o, a fluidez e a viscosidade do pigmento original.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Passo 2: Utilizar s\u00f3lidos polim\u00e9ricos iguais<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O laborat\u00f3rio deve comparar produtos com o mesmo teor de pol\u00edmero ativo antes de otimizar os custos.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Passo 3: Medir v\u00e1rios intervalos de cisalhamento<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O teste deve incluir:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>Viscosidade de Brookfield a baixo cisalhamento<\/li>\n\n\n\n<li>Viscosidade Stormer ou KU<\/li>\n\n\n\n<li>Viscosidade ICI sob alto cisalhamento<\/li>\n\n\n\n<li>Curva de caudal<\/li>\n\n\n\n<li>Tens\u00e3o de escoamento<\/li>\n\n\n\n<li>Recupera\u00e7\u00e3o tixotr\u00f3pica<\/li>\n<\/ul>\n\n\n\n<h3 class=\"wp-block-heading\">Passo 4: Verificar o desempenho da aplica\u00e7\u00e3o<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O laborat\u00f3rio deve realizar os seguintes testes:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>Resist\u00eancia \u00e0 deforma\u00e7\u00e3o<\/li>\n\n\n\n<li>Subida de n\u00edvel<\/li>\n\n\n\n<li>Arrasto do pincel<\/li>\n\n\n\n<li>Sensa\u00e7\u00e3o do rolo<\/li>\n\n\n\n<li>Salpicos<\/li>\n\n\n\n<li>Comportamento da pulveriza\u00e7\u00e3o<\/li>\n\n\n\n<li>Espessura da pel\u00edcula<\/li>\n<\/ul>\n\n\n\n<h3 class=\"wp-block-heading\">Passo 5: Verificar a estabilidade do pigmento<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O programa de testes deve incluir:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>Sedimenta\u00e7\u00e3o<\/li>\n\n\n\n<li>Sin\u00e9rese<\/li>\n\n\n\n<li>Tamanho das part\u00edculas<\/li>\n\n\n\n<li>Desenvolvimento da cor<\/li>\n\n\n\n<li>Brilho<\/li>\n\n\n\n<li>Rub-up<\/li>\n\n\n\n<li>Estabilidade de armazenamento<\/li>\n<\/ul>\n\n\n\n<h3 class=\"wp-block-heading\">Passo 6: Repetir a diferentes temperaturas<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">A realiza\u00e7\u00e3o de ensaios a 25 \u00b0C e a uma temperatura elevada pode revelar a sensibilidade \u00e0 temperatura.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Passo 7: Repetir ap\u00f3s a colora\u00e7\u00e3o<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Os corantes universais cont\u00eam tensioativos e glic\u00f3is que podem alterar o espessamento por associa\u00e7\u00e3o. A tinta colorida pode necessitar de um equil\u00edbrio de espessantes diferente do da base branca.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">O Zhiwei HEC pode substituir o HMHEC?<\/h2>\n\n\n\n<p class=\"wp-block-paragraph\">O HEC convencional n\u00e3o pode substituir automaticamente o HMHEC numa rela\u00e7\u00e3o de um para um.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A Zhiwei disp\u00f5e atualmente de uma vasta gama de modelos convencionais de HEC para revestimentos, incluindo o HEC 15K, o HEC 30K, o HEC 50K, o HEC 100K e o HEC 150K. A empresa descreve o HEC como um espessante n\u00e3o i\u00f3nico que contribui para a viscosidade, a suspens\u00e3o de pigmentos, a fluidez na aplica\u00e7\u00e3o e a estabilidade de armazenamento em revestimentos \u00e0 base de \u00e1gua. <a href=\"https:\/\/zhiweichem.com\/pt\/hec\/hec-para-tintas-latex-para-arquitetura\/\">Zhiwei HEC para tinta l\u00e1tex de arquitetura<\/a><\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Estes graus podem constituir produtos de refer\u00eancia \u00fateis durante um estudo sobre espessantes associativos.<\/p>\n\n\n\n<figure class=\"wp-block-table\"><table class=\"has-fixed-layout\"><thead><tr><th>Objetivo da formula\u00e7\u00e3o<\/th><th>N\u00edvel Inicial de Zhiwei<\/th><th>Fun\u00e7\u00e3o no teste<\/th><\/tr><\/thead><tbody><tr><td>Corpo m\u00e9dio a alto<\/td><td>HEC 30K<\/td><td>Linha de base convencional do HEC<\/td><\/tr><tr><td>Maior viscosidade e suspens\u00e3o<\/td><td>HEC 50K<\/td><td>Linha de base convencional mais elevada do HEC<\/td><\/tr><tr><td>Selec\u00e7\u00e3o de tintas com elevado teor de PVC<\/td><td>HEC 30K ou HEC 50K<\/td><td>Comparar a suspens\u00e3o do pigmento e a sensa\u00e7\u00e3o ao passar o rolo<\/td><\/tr><tr><td>Associa\u00e7\u00e3o hidrof\u00f3bica verdadeira<\/td><td>Nota confirmada no HMHEC<\/td><td>Requer dados expl\u00edcitos sobre a modifica\u00e7\u00e3o hidrof\u00f3bica<\/td><\/tr><\/tbody><\/table><\/figure>\n\n\n\n<p class=\"wp-block-paragraph\">Zhiwei <a href=\"https:\/\/zhiweichem.com\/pt\/produtos\/hec-30k\/\">HEC 30K<\/a> apresenta uma viscosidade Brookfield LV indicada de 1 501-2 600 mPa.s numa solu\u00e7\u00e3o de 1% a 25 \u00b0C.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Zhiwei <a href=\"https:\/\/zhiweichem.com\/pt\/produtos\/hec-50k\/\">HEC 50K<\/a> apresenta uma viscosidade Brookfield LV indicada de 2 601-3 400 mPa.s nas mesmas condi\u00e7\u00f5es especificadas.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Estes valores n\u00e3o podem ser comparados diretamente com as especifica\u00e7\u00f5es medidas \u00e0 concentra\u00e7\u00e3o de 2% nem com outro m\u00e9todo de viscosimetria.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A gama de produtos Zhiwei destinada ao p\u00fablico identifica estes produtos como HEC, e n\u00e3o como HMHEC. Um comprador que necessite especificamente de hidroxietilcelulose modificada hidrofobicamente deve solicitar uma confirma\u00e7\u00e3o por escrito de:<\/p>\n\n\n\n<ul class=\"wp-block-list\">\n<li>Modifica\u00e7\u00e3o hidrof\u00f3bica<\/li>\n\n\n\n<li>Tipo hidrof\u00f3bico<\/li>\n\n\n\n<li>N\u00edvel de modifica\u00e7\u00e3o<\/li>\n\n\n\n<li>M\u00e9todo da viscosidade da solu\u00e7\u00e3o<\/li>\n\n\n\n<li>Viscosidade a baixo cisalhamento<\/li>\n\n\n\n<li>Viscosidade KU<\/li>\n\n\n\n<li>Viscosidade ICI<\/li>\n\n\n\n<li>Resposta associativa com l\u00e1tex<\/li>\n\n\n\n<li>Resposta aos tensioativos<\/li>\n\n\n\n<li>Compatibilidade dos pigmentos<\/li>\n\n\n\n<li>Sensibilidade \u00e0 temperatura<\/li>\n\n\n\n<li>Ordem de adi\u00e7\u00e3o recomendada<\/li>\n\n\n\n<li>TDS, SDS e certificado de an\u00e1lise (COA) do lote<\/li>\n<\/ul>\n\n\n\n<p class=\"wp-block-paragraph\">Esta distin\u00e7\u00e3o refor\u00e7a a credibilidade t\u00e9cnica. Al\u00e9m disso, evita que um HEC comum de elevada viscosidade seja selecionado para uma aplica\u00e7\u00e3o que exija um comportamento verdadeiramente associativo.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Erros comuns na sele\u00e7\u00e3o<\/h2>\n\n\n\n<h3 class=\"wp-block-heading\">Tratar cada HEC como HMHEC<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Um HEC de alta viscosidade n\u00e3o \u00e9 automaticamente modificado de forma hidrof\u00f3bica. O fornecedor deve confirmar a composi\u00e7\u00e3o qu\u00edmica.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Sele\u00e7\u00e3o com base num \u00fanico \u00edndice de viscosidade<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Um \u00fanico valor da solu\u00e7\u00e3o aquosa n\u00e3o descreve a reologia do revestimento. O formulador necessita de medi\u00e7\u00f5es em condi\u00e7\u00f5es de cisalhamento baixo, m\u00e9dio e elevado.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Ignorar o tipo de pigmento<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O carbonato de c\u00e1lcio e o caulim podem apresentar comportamentos de adsor\u00e7\u00e3o diferentes. Uma altera\u00e7\u00e3o na composi\u00e7\u00e3o do pacote de extensores pode exigir um novo equil\u00edbrio do espessante.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Testes apenas na \u00e1gua<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Os ensaios com \u00e1gua avaliam a hidrata\u00e7\u00e3o e a viscosidade b\u00e1sica. N\u00e3o revelam intera\u00e7\u00f5es com l\u00e1tex, dispersantes, pigmentos, tensioativos, antiespumantes e corantes.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Ignorar a temperatura<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">A adsor\u00e7\u00e3o e a viscosidade do HMHEC podem diminuir a temperaturas mais elevadas. O formulador deve testar condi\u00e7\u00f5es realistas de produ\u00e7\u00e3o e armazenamento.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Partir do princ\u00edpio de que um tamanho de part\u00edcula maior implica um fracasso<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Um tamanho hidrodin\u00e2mico de part\u00edcula maior pode resultar de uma camada de pol\u00edmero adsorvido ou de uma rede revers\u00edvel \u00fatil. O resultado deve ser verificado atrav\u00e9s de ensaios de estabilidade, cor e forma\u00e7\u00e3o de pel\u00edcula.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Adicionar HMHEC em excesso<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">A forma\u00e7\u00e3o excessiva de pontes polim\u00e9ricas pode aumentar a flocula\u00e7\u00e3o, a tens\u00e3o de escoamento, o arrasto da escova e prejudicar o nivelamento. Uma maior quantidade de espessante nem sempre garante uma melhor estabilidade.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Medi\u00e7\u00e3o imediatamente ap\u00f3s o cisalhamento elevado<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">A estrutura associativa necessita de tempo para se restabelecer. O m\u00e9todo de ensaio deve especificar um per\u00edodo de recupera\u00e7\u00e3o fixo.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Perguntas mais frequentes<\/h2>\n\n\n\n<h3 class=\"wp-block-heading\">O que \u00e9 o HMHEC?<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O HMHEC \u00e9 uma hidroxietilcelulose que cont\u00e9m uma pequena quantidade de grupos hidrof\u00f3bicos. Estes grupos criam associa\u00e7\u00f5es tempor\u00e1rias entre as cadeias polim\u00e9ricas e os componentes do revestimento.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Como \u00e9 que o HMHEC engrossa a tinta \u00e0 base de \u00e1gua?<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">A estrutura principal do HEC hidrata-se e entrela\u00e7a-se na \u00e1gua. Os grupos hidrof\u00f3bicos tamb\u00e9m formam liga\u00e7\u00f5es revers\u00edveis entre as cadeias polim\u00e9ricas, os pigmentos e as part\u00edculas de l\u00e1tex.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">O HMHEC \u00e9 um espessante associativo?<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Sim. Os seus grupos hidrof\u00f3bicos criam associa\u00e7\u00f5es intermoleculares que contribuem para a reologia do revestimento.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Qual \u00e9 a diferen\u00e7a entre HEC e HMHEC?<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O HEC espessa-se principalmente atrav\u00e9s da hidrata\u00e7\u00e3o e do entrela\u00e7amento das cadeias. O HMHEC tamb\u00e9m cria uma rede associativa hidrof\u00f3bica.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">O HMHEC funciona com carbonato de c\u00e1lcio?<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O HMHEC pode ser fortemente adsorvido pelo carbonato de c\u00e1lcio. O resultado depende do tamanho das part\u00edculas, do tratamento da superf\u00edcie, do pH, do sal, do dispersante e da composi\u00e7\u00e3o qu\u00edmica do pol\u00edmero.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">O HMHEC funciona com caulim?<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">O HMHEC pode ser adsorvido no caulim, mas a intera\u00e7\u00e3o pode diferir da que ocorre com o carbonato de c\u00e1lcio, uma vez que o caulim possui uma estrutura em forma de placas e um comportamento de carga superficial diferente.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">O HMHEC apresenta dilui\u00e7\u00e3o por cisalhamento?<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Sim. O cisalhamento perturba parte da sua rede tempor\u00e1ria e reduz a viscosidade. Parte da viscosidade \u00e9 recuperada quando a taxa de cisalhamento diminui.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">O HMHEC recupera-se imediatamente ap\u00f3s o cisalhamento?<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Nem sempre. A reconstru\u00e7\u00e3o da rede leva tempo, pelo que a curva de cisalhamento decrescente pode diferir da curva de cisalhamento crescente.<\/p>\n\n\n\n<h3 class=\"wp-block-heading\">Qual modelo da Zhiwei deve ser testado?<\/h3>\n\n\n\n<p class=\"wp-block-paragraph\">Os Zhiwei HEC 30K e HEC 50K s\u00e3o tipos de refer\u00eancia HEC convencionais \u00fateis para ensaios de revestimento. Um projeto que exija HMHEC deve solicitar um tipo especificamente confirmado como modificado hidrofobicamente.<\/p>\n\n\n\n<h2 class=\"wp-block-heading\">Conclus\u00e3o<\/h2>\n\n\n\n<p class=\"wp-block-paragraph\">A hidroxietilcelulose modificada hidrofobicamente proporciona um espessamento superior ao da fase aquosa convencional.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A sua estrutura hidrof\u00edlica hidrata-se na \u00e1gua, enquanto os seus grupos hidrof\u00f3bicos formam liga\u00e7\u00f5es tempor\u00e1rias entre as cadeias polim\u00e9ricas e os componentes do revestimento. O HMHEC tamb\u00e9m pode adsorver-se ao carbonato de c\u00e1lcio e ao caulim, contribuindo para a forma\u00e7\u00e3o de uma rede revers\u00edvel entre o pigmento e o pol\u00edmero.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Este mecanismo permite a suspens\u00e3o do pigmento, o armazenamento do produto, o controlo do caudal de aplica\u00e7\u00e3o e a recupera\u00e7\u00e3o da viscosidade. Al\u00e9m disso, torna o HMHEC sens\u00edvel ao tipo de pigmento, ao tamanho das part\u00edculas, \u00e0 temperatura, aos tensioativos, aos dispersantes e ao hist\u00f3rico de cisalhamento.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">A Zhiwei (Jinan) New Materials Co., Ltd. disponibiliza graus convencionais de HEC, tais como o HEC 30K e o HEC 50K, para ensaios de viscosidade de revestimento e de suspens\u00e3o. Estes graus constituem refer\u00eancias fi\u00e1veis para compara\u00e7\u00e3o quando um formulador avalia se o HEC convencional ou um HMHEC verdadeiramente associativo \u00e9 mais adequado.<\/p>\n\n\n\n<p class=\"wp-block-paragraph\">Os clientes podem indicar o tipo de ligante, a concentra\u00e7\u00e3o volum\u00e9trica de pigmento, os teores de carbonato de c\u00e1lcio e caulim, os valores-alvo de viscosidade KU e ICI, o m\u00e9todo de aplica\u00e7\u00e3o, a temperatura de armazenamento e o pacote de espessantes utilizado. A equipa t\u00e9cnica da Zhiwei poder\u00e1, ent\u00e3o, preparar uma f\u00f3rmula espec\u00edfica e um plano de ensaios.<\/p>","protected":false},"excerpt":{"rendered":"<p>Hydrophobically modified hydroxyethyl cellulose thickens water-based paint through two connected mechanisms. Its water-soluble cellulose backbone hydrates and increases the viscosity of the water phase. Its hydrophobic side groups also associate with each other and with hydrophobic surfaces in the coating. These interactions create a temporary three-dimensional network. The network can include polymer chains, latex particles, [&hellip;]<\/p>\n","protected":false},"author":2,"featured_media":2775,"comment_status":"open","ping_status":"open","sticky":false,"template":"","format":"standard","meta":{"_acf_changed":false,"footnotes":""},"categories":[142],"tags":[144,149,147,146,145,143,148],"class_list":["post-2769","post","type-post","status-publish","format-standard","has-post-thumbnail","hentry","category-hmhec","tag-associative-cellulose-thickener","tag-associative-thickener-for-paint","tag-hec-paint-thickener","tag-hmhec-thickener","tag-hmhec-thickening-mechanism","tag-hydrophobically-modified-hydroxyethyl-cellulose","tag-water-based-coating-rheology"],"acf":[],"_links":{"self":[{"href":"https:\/\/zhiweichem.com\/pt\/wp-json\/wp\/v2\/posts\/2769","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/zhiweichem.com\/pt\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/zhiweichem.com\/pt\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/zhiweichem.com\/pt\/wp-json\/wp\/v2\/users\/2"}],"replies":[{"embeddable":true,"href":"https:\/\/zhiweichem.com\/pt\/wp-json\/wp\/v2\/comments?post=2769"}],"version-history":[{"count":0,"href":"https:\/\/zhiweichem.com\/pt\/wp-json\/wp\/v2\/posts\/2769\/revisions"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/zhiweichem.com\/pt\/wp-json\/wp\/v2\/media\/2775"}],"wp:attachment":[{"href":"https:\/\/zhiweichem.com\/pt\/wp-json\/wp\/v2\/media?parent=2769"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/zhiweichem.com\/pt\/wp-json\/wp\/v2\/categories?post=2769"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/zhiweichem.com\/pt\/wp-json\/wp\/v2\/tags?post=2769"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}